| Diameter | 1.75 mm ±0.02 | |
| Density | 1.04 g/cm³ | D792 |
| Melt Flow Rate | 23 g/10min | D1238 (220°C/10kg) |
| Tensile Strength (Yield) | 520 kg/cm² | D638 |
| Elongation at Break | 30 % | D638 |
| Young's Modulus | 22600 kg/cm² | D638 |
| Bending Strength | 800 kg/cm² | D790 |
| Bending Modulus | 28000 kg/cm² | D790 |
| Rockwell Hardness | 110 R | D785 |
| Notched Izod Impact Strength (@23°C) | 20-23 kg·cm/cm | D256 |
| Notched Izod Impact Strength (@-30°C, 6.4mm) | 8 kg·cm/cm | D256 |
| Relative Temperature Index (Electrical) | 60 °C | UL746B |
| Relative Temperature Index (Mechanical with Impact) | 60 °C | UL746B |
| Relative Temperature Index (Mechanical without Impact) | 60 °C | UL746B |
| Heat Deflection Temperature (18.6 kg) | 86 °C | D648 |
| Heat Deflection Temperature (4.6 kg) | 90 °C | D648 |
| Vicat Softening Temperature | 94 °C | D1525 (5kg, 50°C/h) |