KINGROON HS-PETG

Complete technical data sheet with print conditions, material properties, and performance specifications.

Product Information

Version:

Nozzle Temperature	230-260 °C
Bed Temperature	65-75 °C
Cooling Fan	0 - 60%
Retraction Distance	0.8-1.4 mm
Retraction Speed	30-60 mm/s
Build Surface Materials	Smooth PEI Plate, Textured PEI Plate
Support Material	Support for PETG

Diameter	1.75 mm
Density	1.28 g/cm³	ISO 1183
Melt index	25.5-30.9 g/10 min ±2.7
Melting temperature	214 °C	DSC
Glass transition temperature	66 °C	DSC
Vicat softening temperature	70 °C	ISO 306, GB/T 1633
Heat deflection temperature (1.8 MPa)	62 °C	ISO 75
Heat deflection temperature (0.45 MPa)	69 °C	ISO 75
Saturated water absorption	0.4 %
Young's modulus (X-Y)	1620-2000 MPa ±190	ISO 527, GB/T 1040
Young's modulus (Z)	1410-1670 MPa ±130	ISO 527, GB/T 1040
Tensile strength (X-Y)	30-38 MPa ±4	ISO 527, GB/T 1040
Tensile strength (Z)	19-27 MPa ±4	ISO 527, GB/T 1040
Elongation at break (X-Y)	7.4-9.8 % ±1.2	ISO 527, GB/T 1040
Elongation at break (Z)	4.3-5.9 % ±0.8	ISO 527, GB/T 1040
Bending modulus (X-Y)	1930-2170 MPa ±120	ISO 178, GB/T 9341
Bending modulus (Z)	1670-1950 MPa ±140	ISO 178, GB/T 9341
Bending strength (X-Y)	61-67 MPa ±3	ISO 178, GB/T 9341
Bending strength (Z)	44-52 MPa ±4	ISO 178, GB/T 9341
Impact strength (Z), unnotched	9.4-11.8 kJ/m² ±1.2	ISO 179, GB/T 1043
Maximum printing speed	300 mm/s
Impact strength (X-Y), unnotched	29.3-33.7 kJ/m² ±2.2	ISO 179, GB/T 1043
Impact strength (X-Y), notched	4.4-8 kJ/m² ±1.8	ISO 179, GB/T 1043

Chemical resistance: acids	Not resistant	Data Sheet
Chemical resistance: alkalis	Not resistant	Data Sheet
Chemical resistance: organic solvents	Not resistant to some organic solvents	Data Sheet
Chemical resistance: oils and grease	Resistant to most kinds of oil and grease	Data Sheet
Solubility in water	Insoluble in water	Data Sheet