KINGROON PETG

Complete technical data sheet with print conditions, material properties, and performance specifications.

Product Information

Version:

Nozzle Temperature	230-270 °C
Bed Temperature	65-75 °C
Cooling Fan	0 - 60%
Retraction Distance	0.8-1.4 mm
Retraction Speed	30-60 mm/s
Build Surface Materials	Engineering Plate, High Temperature Plate, Textured PEI Plate
Support Material	Support for PLA

Diameter	1.75 mm
Density	1.25 g/cm³	ISO 1183
Melt index	10.2-13.2 g/10 min ±1.5
Melting temperature	228 °C	DSC
Glass transition temperature	70 °C	DSC
Vicat softening temperature	79 °C	ISO 306, GB/T 1633
Heat deflection temperature (1.8 MPa)	68 °C	ISO 75
Heat deflection temperature (0.45 MPa)	74 °C	ISO 75
Saturated water absorption	0.3 %
Young's modulus (X-Y)	1260-1580 MPa ±160	ISO 527, GB/T 1040
Young's modulus (Z)	1090-1370 MPa ±140	ISO 527, GB/T 1040
Tensile strength (X-Y)	29-37 MPa ±4	ISO 527, GB/T 1040
Tensile strength (Z)	26-32 MPa ±3	ISO 527, GB/T 1040
Elongation at break (X-Y)	6.9-9.5 % ±1.3	ISO 527, GB/T 1040
Elongation at break (Z)	4.3-6.1 % ±0.9	ISO 527, GB/T 1040
Bending modulus (X-Y)	1480-1740 MPa ±130	ISO 178, GB/T 9341
Bending modulus (Z)	1410-1630 MPa ±110	ISO 178, GB/T 9341
Bending strength (X-Y)	65-71 MPa ±3	ISO 178, GB/T 9341
Bending strength (Z)	51-59 MPa ±4	ISO 178, GB/T 9341
Impact strength (Z), unnotched	5.4-9 kJ/m² ±1.8	ISO 179, GB/T 1043
Maximum printing speed	220 mm/s
Impact strength (X-Y), unnotched	34.1-40.7 kJ/m² ±3.3	ISO 179, GB/T 1043
Impact strength (X-Y), notched	6.5-10.7 kJ/m² ±2.1	ISO 179, GB/T 1043

Chemical resistance: acids	Not resistant	Data Sheet
Chemical resistance: alkalis	Not resistant	Data Sheet
Chemical resistance: organic solvents	Not resistant to some organic solvents	Data Sheet
Chemical resistance: oils and grease	Resistant to most kinds of oil and grease	Data Sheet
Solubility in water	Insoluble in water	Data Sheet