KINGROON PLA-CF

Complete technical data sheet with print conditions, material properties, and performance specifications.

Product Information

Version:

Nozzle Temperature	210-240 °C
Bed Temperature	35-45 °C
Cooling Fan	Turn on
Retraction Distance	0.6-1 mm
Retraction Speed	20-40 mm/s
Build Surface Materials	Cool Plate, High Temperature Plate, Textured PEI Plate
Support Material	Support for PLA

Diameter	1.75 mm
Density	1.22 g/cm³	ISO 1183
Melt index	3.1-4.3 g/10 min ±0.6
Melting temperature	165 °C	DSC
Glass transition temperature	63 °C	DSC
Vicat softening temperature	69 °C	ISO 306, GB/T 1633
Heat deflection temperature (1.8 MPa)	54 °C	ISO 75
Heat deflection temperature (0.45 MPa)	55 °C	ISO 75
Saturated water absorption	0.42 %
Young's modulus (X-Y)	2670-2910 MPa ±120	ISO 527, GB/T 1040
Young's modulus (Z)	2070-2250 MPa ±90	ISO 527, GB/T 1040
Tensile strength (X-Y)	34-42 MPa ±4	ISO 527, GB/T 1040
Tensile strength (Z)	24-28 MPa ±2	ISO 527, GB/T 1040
Elongation at break (X-Y)	5.2-11.6 % ±3.2	ISO 527, GB/T 1040
Elongation at break (Z)	2.9-4.3 % ±0.7	ISO 527, GB/T 1040
Bending modulus (X-Y)	3760-4140 MPa ±190	ISO 178, GB/T 9341
Bending modulus (Z)	2080-2440 MPa ±180	ISO 178, GB/T 9341
Bending strength (X-Y)	85-93 MPa ±4	ISO 178, GB/T 9341
Bending strength (Z)	46-52 MPa ±3	ISO 178, GB/T 9341
Impact strength (Z), unnotched	7.1-8.5 kJ/m² ±0.7	ISO 179, GB/T 1043
Maximum printing speed	200 mm/s
Impact strength (X-Y), unnotched	19.5-26.9 kJ/m² ±3.7	ISO 179, GB/T 1043
Impact strength (X-Y), notched	5-10.2 kJ/m² ±2.6	ISO 179, GB/T 1043

Chemical resistance: acids	Not resistant	Data Sheet
Chemical resistance: alkalis	Not resistant	Data Sheet
Chemical resistance: organic solvents	Not resistant to some organic solvents	Data Sheet
Chemical resistance: oils and grease	Not resistant to some kinds of oil and grease	Data Sheet
Solubility in water	Insoluble in water	Data Sheet