Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Overture | |
| Product Name | Nylon | |
| Filament Type | Nylon | |
| Finish | Standard |
| Nozzle Temperature | 250-270 °C | |
| Bed Temperature | 25-50 °C | |
| Print Speed | 30-50 mm/s | |
| Cooling Fan | Off | |
| Retraction Distance | 3-6 mm | |
| Retraction Speed | 40-60 mm/s | |
| Build Surface Materials | PA film, PI film | |
| Support Material | None |
| Diameter | 1.75 mm ±0.02 | |
| Density | 1.13 g/cm³ | ISO 1183 |
| Glass Transition Temperature | 67 °C | DSC, 10°C/min |
| Vicat Softening Temperature | 180 °C | ISO 306 |
| Melt Index | 12 g/10 min | ISO 1133 |
| Melting Temperature | 190 °C | DSC, 10°C/min |
| Crystallization Temperature | 128 °C | DSC, 10°C/min |
| Decomposition Temperature | 370 °C | TGA, 20°C/min |
| Young's Modulus (X-Y) | 2223 MPa ±199 | ISO 527 |
| Tensile Strength (X-Y) | 66.2 MPa ±0.9 | ISO 527 |
| Elongation at Break (X-Y) | 9.9 % ±1.5 | ISO 527 |
| Bending Modulus (X-Y) | 1667 MPa ±118 | ISO 178 |
| Bending Strength (X-Y) | 97 MPa ±1.1 | ISO 178 |
| Charpy Impact Strength (X-Y) | 9.6 kJ/m² ±1.4 | ISO 179 |
| Technical Data Sheet | View Data Sheet |