Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Overture | |
| Product Name | Air PLA | |
| Filament Type | PLA | |
| Finish | Standard |
| Nozzle Temperature | 190-210 °C | |
| Bed Temperature | 25-60 °C | |
| Print Speed | 30-50 mm/s | |
| Cooling Fan | On | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s | |
| Build Surface Materials | OVERTURE Build Surface, Textured PEI |
| Density | 0.82 g/cm³ | ISO 1183, GB/T 1033 |
| Vicat softening temperature | 60.1 °C | ISO 306, GB/T 1633 |
| Melting temperature | 151.4 °C | DSC, 10 °C/min |
| Young's modulus (X-Y) | 1685 MPa ±81 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 25.1 MPa ±0.5 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 21.3 MPa ±0.6 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 8.2 % ±0.4 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 1965 MPa ±72 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 52.1 MPa ±2.5 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 2.6 kJ/m² ±0.4 | ISO 179, GB/T 1043 |
| Technical Data Sheet | View Data Sheet | Version 5.1 · 2024-07 |