Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Overture | |
| Product Name | PLA Carbon Fiber | |
| Filament Type | PLA | |
| Finish | Carbon Fiber |
| Nozzle Temperature | 190-220 °C | |
| Bed Temperature | 30-60 °C | |
| Print Speed | 30-70 mm/s | |
| Cooling Fan | On | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 30-60 mm/s | |
| Build Surface Materials | Overture Build Surface, Glass, Blue Tape | |
| Support Material | None |
| Diameter | 1.75 mm ±0.02 | |
| Density | 1.29 g/cm³ | ISO 1183 |
| Glass Transition Temperature | 61.9 °C | DSC, 10°C/min |
| Vicat Softening Temperature | 64 °C | ISO 306 |
| Melt Index | 9.24 g/10 min | ISO 1133 |
| Melting Temperature | 162.4 °C | DSC, 10°C/min |
| Young's Modulus (X-Y) | 2945.26 MPa ±100.13 | ISO 527 |
| Tensile Strength (X-Y) | 28.28 MPa ±0.7 | ISO 527 |
| Elongation at Break (X-Y) | 4.2 % ±0.12 | ISO 527 |
| Bending Modulus | 3215.92 MPa ±182.61 | ISO 178 |
| Bending Strength | 54.2 MPa ±1.4 | ISO 178 |
| Young's Modulus (Z) | 2141.33 MPa ±91.06 | ISO 527 |
| Tensile Strength (Z) | 12.54 MPa ±0.68 | ISO 527 |
| Elongation at Break (Z) | 0.75 % ±0.08 | ISO 179 |
| Impact Strength | 4.82 kJ/m² ±0.14 | ISO 179 |