| Manufacturer | Overture | |
| Product Name | PLA Matte | |
| Filament Type | PLA | |
| Finish | Matte |
| Nozzle Temperature | 190-220 °C | |
| Bed Temperature | 30-60 °C | |
| Print Speed | 50-100 mm/s | |
| Cooling Fan | On | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 30-60 mm/s | |
| Build Surface Materials | Overture Build Surface, Glass, Blue Tape | |
| Support Material | None |
| Diameter | 1.75 mm ±0.02 | |
| Density | 1.32 g/cm³ ±0.1 | ISO 1183 |
| Glass Transition Temperature | 61 °C | DSC, 10°C/min |
| Vicat Softening Temperature | 62.7 °C ±0.4 | ISO 306 |
| Melt Index | 25 g/10 min | ISO 1133 |
| Melting Temperature | 150 °C | DSC, 10°C/min |
| Young's Modulus (X-Y) | 1882 MPa ±141.12 | ISO 527 |
| Tensile Strength (X-Y) | 20.9 MPa ±1.95 | ISO 527 |
| Elongation at Break (X-Y) | 34.45 % ±8.06 | ISO 527 |
| Bending Modulus | 2694 MPa ±541.18 | ISO 178 |
| Bending Strength | 39.6 MPa ±1.11 | ISO 178 |
| Charpy Impact Strength | 5.66 kJ/m² ±0.44 | ISO 179 |
| Tensile Strength (Z) | 18.01 MPa ±0.29 | ISO 527 |