Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolyLite ABS | |
| Filament Type | ABS | |
| Finish | Standard |
| Nozzle Temperature | 245-265 °C | |
| Bed Temperature | 90-100 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | OFF | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s |
| Density | 1.04 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 9-14 g/10 min | 220 °C, 2.16kg |
| Glass transition temperature | 101 °C | DSC, 10 °C/min |
| Decomposition temperature | 380 °C | TGA, 20 °C/min |
| Vicat softening temperature | 104 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 98 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 100 °C | ISO 75 |
| Young's modulus (X-Y) | 2246.6 MPa ±58.2 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2080.9 MPa ±92.7 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 33.4 MPa ±0.6 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 29.7 MPa ±0.3 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 17.9 % ±1.3 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 3.1 % ±0.3 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2127.2 MPa ±29.9 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 56.2 MPa ±0.3 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 18 kJ/m² ±0.9 | ISO 179, GB/T |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Good | Data Sheet |
| Resistance to strong alkalis | Fair | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.5 · 2025-07 |