| Manufacturer | Polymaker | |
| Product Name | Polymaker ABS Pro | |
| Filament Type | ABS | |
| Finish | Enhanced |
| Nozzle Temperature | 270-290 °C | |
| Bed Temperature | 100-110 °C | |
| Cooling Fan | 0-30% | |
| Retraction Distance | 1 mm | |
| Retraction Speed | 20 mm/s | |
| Support Material | excellent printing quality |
| Density | 1.04 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 11.1 g/10 min | 210 °C, 2.16 kg |
| Glass transition temperature | 114.9 °C | DSC, 10 °C/min |
| Decomposition temperature | 436.4 °C | TGA, 20 °C/min |
| Vicat softening temperature | 116.1 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (0.45 MPa) | 106.4 °C | ISO 75 |
| Heat deflection temperature (1.8 MPa) | 101.4 °C | ISO 75 |
| Young's modulus (X-Y) | 2330 MPa ±30 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1950 MPa ±20 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 34.94 MPa ±0.62 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 21.87 MPa ±0.32 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 7.34 % ±1.13 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 1.54 % ±0.13 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2330 MPa ±50 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 2170 MPa ±10 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 60.05 MPa ±0.46 | ISO 178, GB/T 9341 |
| Bending strength (Z) | 41.24 MPa ±2.14 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 14.48 kJ/m² ±0.96 | ISO 179, GB/T 1043 |
| Notched Charpy impact strength (X-Y) (moisture conditioned) | 8.87 kJ/m² ±1.14 | ISO 179, GB/T 1043 |
| Notched Charpy impact strength (Z) (moisture conditioned) | 39.58 kJ/m² ±12.45 | ISO 179, GB/T 1043 |
| Technical Data Sheet | View Data Sheet | Version 1.0 · 2026-05-29 |
| Polymaker ABS Pro TDS page on wiki.polymaker.com | Open link | |