| Manufacturer | Polymaker | |
| Product Name | Fiberon ASA-CF08 | |
| Filament Type | ASA | |
| Finish | Carbon Fiber |
| Nozzle Temperature | 260-280 °C | |
| Bed Temperature | 90-100 °C | |
| Print Speed | 350 mm/s | |
| Cooling Fan | OFF |
| Density | 1.09 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 13.9 g/10 min | 240 °C, 5 kg |
| Glass transition temperature | 106.6 °C | DSC, 10 °C/min |
| Decomposition temperature | 328.4 °C | TGA, 20 °C/min |
| Vicat softening temperature | 110.8 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 97.3 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 103 °C | ISO 75 |
| Young's modulus (X-Y) | 3611.7 MPa ±181.1 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1903.8 MPa ±71 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 43.5 MPa ±0.7 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 25 MPa ±0.4 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 1.8 % ±0.1 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 2.7 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 3265 MPa ±56.5 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 1743.4 MPa ±59.9 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 69.1 MPa ±1.62 | ISO 306, GB/T 1633 |
| Bending strength (Z) | 46.5 MPa ±0.8 | ISO 306, GB/T 1633 |
| Notched Charpy impact strength (X-Y) | 5.5 kJ/m² ±0.14 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) | 11 kJ/m² ±0.5 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) | 11.9 kJ/m² ±0.9 | ISO 179, GB/T 1043 |
| Flame retardancy | HB | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.0 · 2025-09 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2025-07-17 |
| Fiberon ASA-CF08 TDS page on wiki.polymaker.com | Open link | |