Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolyLite ASA | |
| Filament Type | ASA | |
| Finish | Standard |
| Nozzle Temperature | 230-260 °C | |
| Bed Temperature | 75-95 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | OFF | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s |
| Density | 1.13 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 25 g/10 min | 220 °C, 10kg |
| Glass transition temperature | 98 °C | DSC, 10 °C/min |
| Vicat softening temperature | 105 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 100 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 103 °C | ISO 75 |
| Young's modulus (X-Y) | 2379 MPa ±157 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1965 MPa ±136 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 43.8 MPa ±0.8 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 32 MPa ±1.8 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 6.7 % ±0.6 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 1.65 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 3206 MPa ±108 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 73.4 MPa ±2.1 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 10.3 kJ/m² ±0.4 | ISO 179, GB/T 1043 |
| Notched Charpy impact strength (Z) | 6.7 kJ/m² ±1.4 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Good | Data Sheet |
| Resistance to strong alkalis | Fair | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 6.0 · 2026-09 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2019-04-17 |
| PolyLite ASA TDS page on wiki.polymaker.com | Open link | |
| PolyLite ASA on us.polymaker.com | Open link |