Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolyMide CoPA | |
| Filament Type | Nylon | |
| Finish | Standard |
| Nozzle Temperature | 250-270 °C | |
| Bed Temperature | 25-50 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | OFF | |
| Retraction Distance | 3-6 mm | |
| Retraction Speed | 40-60 mm/s | |
| Support Material | PolyDissolve S1 |
| Density | 1.12 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 12 g/10 min | 260 °C, 1.2 kg |
| Glass transition temperature | 66 °C | DSC, 10 °C/min |
| Melting temperature | 189 °C | DSC, 10 °C/min |
| Crystallization temperature | 148 °C | DSC, 10 °C/min |
| Decomposition temperature | 370 °C | TGA, 20 °C/min |
| Vicat softening temperature | 180 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 70 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 111 °C | ISO 75 |
| Young's modulus (X-Y) | 2703 MPa ±259 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2209 MPa ±59 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 78 MPa ±0.7 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 45.8 MPa ±1.5 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 12.7 % ±2.1 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 1.3 % ±0.1 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2510 MPa ±25 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 109.8 MPa ±1.3 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 6.9 kJ/m² ±1.4 | ISO 179, GB/T 1043 |
| Young's modulus (X-Y) (moisture conditioned) | 724 MPa ±61 | ISO 527, GB/T 1040 |
| Young's modulus (Z) (moisture conditioned) | 660 MPa ±29 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) (moisture conditioned) | 34.3 MPa ±2.5 | ISO 527, GB/T 1040 |
| Tensile strength (Z) (moisture conditioned) | 13.7 MPa ±1.2 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) (moisture conditioned) | 13.2 % ±2.3 | ISO 527, GB/T 1040 |
| Elongation at break (Z) (moisture conditioned) | 1.7 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) (moisture conditioned) | 636 MPa ±11 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) (moisture conditioned) | 22.6 MPa ±0.5 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) (moisture conditioned) | 27.7 kJ/m² ±1.2 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Poor | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Fair | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |
| Safety Data Sheet | View Safety Sheet | Version 1.1 · 2022-11-29 |
| PolyMide CoPA TDS page on wiki.polymaker.com | Open link | |
| PolyMide CoPA on us.polymaker.com | Open link |