Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | Fiberon PA12-CF10 | |
| Filament Type | PA12 | |
| Finish | Carbon Fiber |
| Nozzle Temperature | 280-300 °C | |
| Bed Temperature | 40-50 °C | |
| Print Speed | 300 mm/s | |
| Cooling Fan | OFF |
| Density | 1.06 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 25 g/10 min | 280 °C, 2.16 kg |
| Glass transition temperature | 55 °C | DSC, 10 °C/min |
| Melting temperature | 171 °C | DSC, 10 °C/min |
| Crystallization temperature | 120 °C | DSC, 10 °C/min |
| Decomposition temperature | 445.2 °C | TGA, 20 °C/min |
| Vicat softening temperature | 170.2 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 105 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 131 °C | ISO 75 |
| Young's modulus (X-Y) | 3311.2 MPa ±134.9 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1806.6 MPa ±145.7 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 77.4 MPa ±1.1 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 52.2 MPa ±0.8 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 4.2 % ±0.4 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 5 % ±1 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2886.5 MPa ±144.8 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 1452.8 MPa ±96.5 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 112.4 MPa ±1 | ISO 178, GB/T 9341 |
| Bending strength (Z) | 69.8 MPa ±2.2 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 9.9 kJ/m² ±0.7 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) | 33.7 kJ/m² ±1.4 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) | 27.6 kJ/m² ±3.7 | ISO 179, GB/T 1043 |
| Young's modulus (X-Y) (moisture conditioned) | 3131.7 MPa ±124.2 | ISO 527, GB/T 1040 |
| Young's modulus (Z) (moisture conditioned) | 1622 MPa ±71.7 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) (moisture conditioned) | 71.7 MPa ±0.7 | ISO 527, GB/T 1040 |
| Tensile strength (Z) (moisture conditioned) | 42.1 MPa ±1.8 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) (moisture conditioned) | 5.3 % ±0.3 | ISO 527, GB/T 1040 |
| Elongation at break (Z) (moisture conditioned) | 5.3 % ±1.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) (moisture conditioned) | 2652.7 MPa ±57.2 | ISO 178, GB/T 9341 |
| Bending modulus (Z) (moisture conditioned) | 1145.9 MPa ±76.9 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) (moisture conditioned) | 91.8 MPa ±1.5 | ISO 178, GB/T 9341 |
| Bending strength (Z) (moisture conditioned) | 52.2 MPa ±1.5 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) (moisture conditioned) | 10.2 kJ/m² ±0.8 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) (moisture conditioned) | 41.2 kJ/m² ±4.4 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) (moisture conditioned) | 20.6 kJ/m² ±4.7 | ISO 179, GB/T 1043 |
| Flame retardancy | HB | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.1 · 2025-01 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2020-10-29 |
| Fiberon PA12-CF10 TDS page on wiki.polymaker.com | Open link | |
| Fiberon PA12-CF10 on us.polymaker.com | Open link |