Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | Fiberon PA6-CF20 | |
| Filament Type | PA6 | |
| Finish | Carbon Fiber |
| Nozzle Temperature | 280-300 °C | |
| Bed Temperature | 40-50 °C | |
| Print Speed | 300 mm/s | |
| Cooling Fan | OFF |
| Density | 1.17 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 20.5 g/10 min | 300 °C, 2.16 kg |
| Glass transition temperature | 74.2 °C | DSC, 10 °C/min |
| Melting temperature | 218.5 °C | DSC, 10 °C/min |
| Crystallization temperature | 184.6 °C | DSC, 10 °C/min |
| Decomposition temperature | 446.2 °C | TGA, 20 °C/min |
| Vicat softening temperature | 219.2 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 173 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 215 °C | ISO 75 |
| Young's modulus (X-Y) | 8636.5 MPa ±211.4 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 3759.5 MPa ±118.5 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 109.3 MPa ±2.4 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 54 MPa ±5.2 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 2.1 % ±0.2 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 1.9 % ±0.4 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 7037.6 MPa ±205.4 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 2975.3 MPa ±174.3 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 161 MPa ±3.9 | ISO 178, GB/T 9341 |
| Bending strength (Z) | 71.3 MPa ±17.7 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 11 kJ/m² ±0.3 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) | 24 kJ/m² ±1 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) | 7.5 kJ/m² ±2.7 | ISO 179, GB/T 1043 |
| Young's modulus (X-Y) (moisture conditioned) | 2508.1 MPa ±82.6 | ISO 527, GB/T 1040 |
| Young's modulus (Z) (moisture conditioned) | 1056.1 MPa ±127.9 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) (moisture conditioned) | 54.7 MPa ±1.1 | ISO 527, GB/T 1040 |
| Tensile strength (Z) (moisture conditioned) | 25.5 MPa ±1.2 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) (moisture conditioned) | 7 % ±0.9 | ISO 527, GB/T 1040 |
| Elongation at break (Z) (moisture conditioned) | 6.7 % ±1.7 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) (moisture conditioned) | 2286.2 MPa ±185.2 | ISO 178, GB/T 9341 |
| Bending modulus (Z) (moisture conditioned) | 801.1 MPa ±24.1 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) (moisture conditioned) | 64.9 MPa ±4.9 | ISO 178, GB/T 9341 |
| Bending strength (Z) (moisture conditioned) | 29.2 MPa ±1 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) (moisture conditioned) | 35.6 kJ/m² ±1.2 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) (moisture conditioned) | 73 kJ/m² ±2 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) (moisture conditioned) | 25.2 kJ/m² ±3.2 | ISO 179, GB/T 1043 |
| Flame retardancy | HB | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.1 · 2024-12 |
| Safety Data Sheet | View Safety Sheet | Version 2.0 · 2024-10-31 |
| Fiberon PA6-CF20 TDS page on wiki.polymaker.com | Open link | |