Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | Fiberon PA6-GF25 | |
| Filament Type | PA6 | |
| Finish | Glass Fiber |
| Nozzle Temperature | 280-300 °C | |
| Bed Temperature | 40-50 °C | |
| Print Speed | 300 mm/s | |
| Cooling Fan | OFF |
| Density | 1.2 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 15.9 g/10 min | 300 °C, 2.16 kg |
| Glass transition temperature | 70.4 °C | DSC, 10 °C/min |
| Melting temperature | 214.5 °C | DSC, 10 °C/min |
| Crystallization temperature | 174.5 °C | DSC, 10 °C/min |
| Decomposition temperature | 437.1 °C | TGA, 20 °C/min |
| Vicat softening temperature | 211.7 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 157 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 191 °C | ISO 75 |
| Young's modulus (X-Y) | 5356.9 MPa ±211 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 3375.9 MPa ±142.1 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 80.1 MPa ±1.8 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 60.7 MPa ±1.1 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 2.4 % ±0.2 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 4 % ±0.4 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 4314.2 MPa ±120.6 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 2849.5 MPa ±282.1 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 133.8 MPa ±4.7 | ISO 178, GB/T 9341 |
| Bending strength (Z) | 99.9 MPa ±3.2 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 10 kJ/m² ±0.7 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) | 27.4 kJ/m² ±0.5 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) | 16.2 kJ/m² ±4 | ISO 179, GB/T 1043 |
| Young's modulus (X-Y) (moisture conditioned) | 1793.6 MPa ±83.9 | ISO 527, GB/T 1040 |
| Young's modulus (Z) (moisture conditioned) | 1164.7 MPa ±117.7 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) (moisture conditioned) | 40.2 MPa ±2.1 | ISO 527, GB/T 1040 |
| Tensile strength (Z) (moisture conditioned) | 26.3 MPa ±1.5 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) (moisture conditioned) | 4.2 % ±0.7 | ISO 527, GB/T 1040 |
| Elongation at break (Z) (moisture conditioned) | 7.1 % ±0.9 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) (moisture conditioned) | 1448.1 MPa ±38.5 | ISO 178, GB/T 9341 |
| Bending modulus (Z) (moisture conditioned) | 836.3 MPa ±22.6 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) (moisture conditioned) | 47.8 MPa ±1.2 | ISO 178, GB/T 9341 |
| Bending strength (Z) (moisture conditioned) | 33.8 MPa ±0.8 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) (moisture conditioned) | 28 kJ/m² ±1 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) (moisture conditioned) | 82.1 kJ/m² ±2.9 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) (moisture conditioned) | 17.5 kJ/m² ±2.4 | ISO 179, GB/T 1043 |
| Flame retardancy | HB | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.1 · 2024-12 |
| Safety Data Sheet | View Safety Sheet | Version 2.0 · 2024-10-31 |
| Fiberon PA6-GF25 TDS page on wiki.polymaker.com | Open link | |
| Fiberon PA6-GF25 on us.polymaker.com | Open link |