Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | Fiberon PA612-ESD | |
| Filament Type | PA612 | |
| Finish | ESD Safe |
| Nozzle Temperature | 280-300 °C | |
| Bed Temperature | 40-50 °C | |
| Print Speed | 300 mm/s | |
| Cooling Fan | OFF |
| Density | 1.1 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 17.4 g/10 min | 275 °C, 5 kg |
| Glass transition temperature | 41.8 °C | DSC, 10 °C/min |
| Melting temperature | 187.3 °C | DSC, 10 °C/min |
| Crystallization temperature | 180.3 °C | DSC, 10 °C/min |
| Decomposition temperature | 441 °C | TGA, 20 °C/min |
| Vicat softening temperature | 190 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 125.4 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 157 °C | ISO 75 |
| Young's modulus (X-Y) | 4293.7 MPa ±116.4 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1784.4 MPa ±102.8 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 84.3 MPa ±2.3 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 21.5 MPa ±2.7 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 3 % ±0.1 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 1.4 % ±0.1 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 3745.5 MPa ±292.6 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 1362.3 MPa ±111.7 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 116.2 MPa ±5.9 | ISO 178, GB/T 9341 |
| Bending strength (Z) | 39.5 MPa ±1.5 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 5.9 kJ/m² ±0.4 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) | 24.1 kJ/m² ±2.4 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) | 4.5 kJ/m² ±0.2 | ISO 179, GB/T 1043 |
| Young's modulus (X-Y) (moisture conditioned) | 3730.8 MPa ±156.2 | ISO 527, GB/T 1040 |
| Young's modulus (Z) (moisture conditioned) | 1343.9 MPa ±99.5 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) (moisture conditioned) | 73.6 MPa ±2.3 | ISO 527, GB/T 1040 |
| Tensile strength (Z) (moisture conditioned) | 19.2 MPa ±1.6 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) (moisture conditioned) | 4.2 % ±0.4 | ISO 527, GB/T 1040 |
| Elongation at break (Z) (moisture conditioned) | 1.9 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) (moisture conditioned) | 3056.1 MPa ±175.5 | ISO 178, GB/T 9341 |
| Bending modulus (Z) (moisture conditioned) | 1420.1 MPa ±114 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) (moisture conditioned) | 102.6 MPa ±4.8 | ISO 178, GB/T 9341 |
| Bending strength (Z) (moisture conditioned) | 40.5 MPa ±1.3 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) (moisture conditioned) | 4.9 kJ/m² ±0.3 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) (moisture conditioned) | 33.6 kJ/m² ±2 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) (moisture conditioned) | 3.6 kJ/m² ±0.1 | ISO 179, GB/T 1043 |
| Flame retardancy | HB | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.0 · 2025-06 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2025-08 |
| Fiberon PA612-ESD TDS page on wiki.polymaker.com | Open link | |
| Fiberon PA612-ESD on us.polymaker.com | Open link |