| Manufacturer | Polymaker | |
| Product Name | PolyLite PC | |
| Filament Type | PC | |
| Finish | Standard |
| Nozzle Temperature | 250-270 °C | |
| Bed Temperature | 90-105 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | OFF | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s |
| Density | 1.19 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 8-11 g/10 min | 260 °C, 2.16kg |
| Light transmission | 89 % | GB/T 2410 |
| Glass transition temperature | 113 °C | DSC, 10 °C/min |
| Decomposition temperature | 360 °C | TGA, 20 °C/min |
| Vicat softening temperature | 120 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 107 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 111 °C | ISO 75 |
| Young's modulus (X-Y) | 2497 MPa ±154 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2371 MPa ±55 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 69.1 MPa ±3 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 52.8 MPa ±1.7 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 4.8 % ±0.9 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 2.7 % ±0.1 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2640 MPa ±47 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 106.1 MPa ±1.6 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 4.1 kJ/m² ±0.9 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Fair | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2019-07-29 |
| PolyLite PC TDS page on wiki.polymaker.com | Open link | |