Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolyMax PC | |
| Filament Type | PC | |
| Finish | Engineered |
| Nozzle Temperature | 250-270 °C | |
| Bed Temperature | 90-105 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | OFF | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s |
| Density | 1.19 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 6-8 g/10 min | 260 °C, 1.2 kg |
| Glass transition temperature | 113 °C | DSC, 10 °C/min |
| Decomposition temperature | 360 °C | TGA, 20 °C/min |
| Vicat softening temperature | 117 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 99 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 114 °C | ISO 75 |
| Young's modulus (X-Y) | 2435 MPa ±63 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2149 MPa ±119 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 53.44 MPa ±0.6 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 41.43 MPa ±1.5 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 4.53 % ±0.45 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 2.79 % ±0.21 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2050 MPa ±79 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 81.29 MPa ±1.53 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 21.28 kJ/m² ±1.69 | ISO 179, GB/T 1043 |
| Low-temperature impact strength (X-Y) | 9.2 kJ/m² ±1.5 | ISO 179-1/1eA:2010, - |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Fair | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |