Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolyMax PC-FR | |
| Filament Type | PC | |
| Finish | Fire Retardant |
| Nozzle Temperature | 250-270 °C | |
| Bed Temperature | 90-105 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | OFF | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s |
| Density | 1.2 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 12-17 g/10 min | 260 °C, 5 kg |
| Glass transition temperature | 115 °C | DSC, 10 °C/min |
| Vicat softening temperature | 116 °C | ISO 306 GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 107 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 110 °C | ISO 75 |
| Young's modulus (X-Y) | 2634 MPa ±182 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2743 MPa ±72 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 67 MPa ±4.5 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 46 MPa ±4.8 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 3.49 % ±0.7 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 2.2 % ±0.3 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2518 MPa ±53 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 96.6 MPa ±1.3 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 11.7 kJ/m² ±1.6 | ISO 179, GB/T 1043 |
| Low-temperature impact strength (X-Y) | 7.5 kJ/m² ±1.6 | ISO 179-1/1eA:2010 |
| Flame retardancy | V0 | Data Sheet |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Fair | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |