Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | Fiberon PETG-ESD | |
| Filament Type | PETG | |
| Finish | ESD Safe |
| Nozzle Temperature | 250-290 °C | |
| Bed Temperature | 70-80 °C | |
| Print Speed | 500 mm/s | |
| Cooling Fan | OFF |
| Density | 1.24 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 14 g/10 min | 280 °C, 5 kg |
| Glass transition temperature | 77 °C | DSC, 10 °C/min |
| Decomposition temperature | 373 °C | TGA, 20 °C/min |
| Vicat softening temperature | 86 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 72 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 76 °C | ISO 75 |
| Young's modulus (X-Y) | 1983 MPa ±74.9 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1626.4 MPa ±31.5 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 36.1 MPa ±0.9 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 20.7 MPa ±0.6 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 7.3 % ±0.7 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 1.8 % ±0.1 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 1650.8 MPa ±140.7 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 1150.9 MPa ±75.6 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 54 MPa ±2.5 | ISO 306, GB/T 1633 |
| Bending strength (Z) | 24.1 MPa ±1.2 | ISO 306, GB/T 1633 |
| Notched Charpy impact strength (X-Y) | 5.7 kJ/m² ±0.5 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) | 29.3 kJ/m² ±2.2 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) | 5.2 kJ/m² ±0.7 | ISO 179, GB/T 1043 |
| Flame retardancy | HB | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.1 · 2024-12 |