Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolyLite PETG | |
| Filament Type | PETG | |
| Finish | Standard |
| Nozzle Temperature | 230-260 °C | |
| Bed Temperature | 70-80 °C | |
| Print Speed | 50-100 mm/s | |
| Cooling Fan | OFF-20% | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s | |
| Support Material | PolyDissolve S1 |
| Density | 1.25 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 10.8 g/10 min | 240 °C, 2.16kg |
| Light transmission | 90 % | GB/T 2410 |
| Glass transition temperature | 81 °C | DSC, 10 °C/min |
| Vicat softening temperature | 84 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 75 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 78 °C | ISO 75 |
| Young's modulus (X-Y) | 2116.8 MPa ±68.1 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1898.7 MPa ±98.5 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 50.8 MPa ±0.9 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 42.8 MPa ±2.8 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 8.4 % ±1.7 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 3.3 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 1898.5 MPa ±35.5 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 69.6 MPa ±0.8 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 2.6 kJ/m² ±0.2 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Fair | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2019-07-29 |
| PolyLite PETG TDS page on wiki.polymaker.com | Open link | |
| PolyLite PETG on us.polymaker.com | Open link |