| Manufacturer | Polymaker | |
| Product Name | Panchroma Matte PLA | |
| Filament Type | PLA | |
| Finish | Matte |
| Nozzle Temperature | 190-230 °C | |
| Bed Temperature | 25-60 °C | |
| Print Speed | 30-300 mm/s | |
| Cooling Fan | On | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s | |
| Build Surface Materials | Glass, PEI |
| Diameter | 1.75-2.85 mm ±0.03 | |
| Density | 1.31 g/cm³ | ISO 1183 |
| Melt Flow Rate | 14-20 g/10 min | ISO 1133, 210°C, 2.16kg |
| Water Absorption | 0.36 % | |
| Glass Transition Temperature | 60.6 °C | DSC, 10°C/min |
| Melting Temperature | 162.6 °C | DSC |
| Vicat Softening Temperature | 62.7 °C | ISO 306 |
| Heat Deflection Temperature @ 1.8MPa | 52 °C | ISO 75 |
| Heat Deflection Temperature @ 0.45MPa | 57.8 °C | ISO 75 |
| Young's Modulus (X-Y) | 1997 MPa ±64 | ISO 527 |
| Young's Modulus (Z) | 1615 MPa ±54 | ISO 527 |
| Tensile Strength (X-Y) | 23.2 MPa ±0.5 | ISO 527 |
| Tensile Strength (Z) | 12.2 MPa ±0.7 | ISO 527 |
| Elongation at Break (X-Y) | 27.8 % ±2.4 | ISO 527 |
| Elongation at Break (Z) | 0.9 % ±0.1 | ISO 527 |
| Bending Modulus (X-Y) | 2209 MPa ±75 | ISO 178 |
| Bending Strength (X-Y) | 40.4 MPa ±1.1 | ISO 178 |
| Charpy Impact Strength (X-Y) | 6.7 kJ/m² ±0.5 | ISO 179 |
| Industrial Compostable | 1 Yes |