Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolyLite PLA | |
| Filament Type | PLA | |
| Finish | Standard |
| Nozzle Temperature | 190-230 °C | |
| Bed Temperature | 25-60 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | ON | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s | |
| Build Surface Materials | PC, Texture PEI |
| Diameter | 1.75-2.85 mm ±0.03 | |
| Density | 1.17 g/cm³ | ISO1183, GB/T1033 |
| Melt Index | 7-11 g/10 min | 210°C, 2.16kg |
| Glass Transition Temperature | 61 °C | DSC, 10°C/min |
| Melting Temperature | 150 °C | DSC, 10°C/min |
| Crystallization Temperature | 114 °C | DSC, 10°C/min |
| Decomposition Temperature | 325 °C | TGA, 20°C/min |
| Vicat Softening Temperature | 63 °C | ISO 306, GB/T 1633 |
| Heat Deflection Temperature @ 1.8MPa | 58 °C | ISO 75 1.8MPa |
| Heat Deflection Temperature @ 0.45MPa | 60 °C | ISO 75 0.45MPa |
| Young's Modulus (X-Y) | 3426.9 MPa ±64.8 | ISO 527, GB/T 1040 |
| Young's Modulus (Z) | 3064.9 MPa ±83.4 | ISO 527, GB/T 1040 |
| Tensile Strength (X-Y) | 52.3 MPa ±0.3 | ISO 527, GB/T 1040 |
| Tensile Strength (Z) | 40.5 MPa ±0.5 | ISO 527, GB/T 1040 |
| Elongation at Break (X-Y) | 6.3 % ±0.6 | ISO 527, GB/T 1040 |
| Elongation at Break (Z) | 1.8 % ±0.1 | ISO 527, GB/T 1040 |
| Bending Modulus (X-Y) | 3230.9 MPa ±55.3 | ISO 178, GB/T 9341 |
| Bending Strength (X-Y) | 86.9 MPa ±1.2 | ISO 178, GB/T 9341 |
| Notched Charpy Impact Strength (X-Y) | 3.3 kJ/m² ±0.2 | ISO 179, GB/T 1043 |
| Effect of Weak Acids | Good | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/pla/polylite-tm-pla |
| Effect of Strong Acids | Poor | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/pla/polylite-tm-pla |
| Effect of Weak Alkalis | Fair | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/pla/polylite-tm-pla |
| Effect of Strong Alkalis | Poor | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/pla/polylite-tm-pla |
| Effect of Oils and Grease | Good | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/pla/polylite-tm-pla |
| Technical Data Sheet | View Data Sheet(Version v5.3) |