| Manufacturer | Polymaker | |
| Product Name | PolyLite PLA-CF | |
| Filament Type | PLA | |
| Finish | Carbon Fiber |
| Nozzle Temperature | 190-230 °C | |
| Bed Temperature | 25-60 °C | |
| Print Speed | 50-300 mm/s | |
| Cooling Fan | ON | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s | |
| Support Material | PolySupport and PolyDissolve S1 |
| Density | 1.29 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 9.2 g/10 min | 210 °C, 2.16 kg |
| Glass transition temperature | 62 °C | DSC, 10 °C/min |
| Melting temperature | 162 °C | DSC, 10 °C/min |
| Vicat softening temperature | 64 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 50 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 54 °C | ISO 75 |
| Young's modulus (X-Y) | 3280.7 MPa ±79.6 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2213.1 MPa ±42.9 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 31.2 MPa ±0.7 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 15.1 MPa ±0.7 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 13.2 % ±1.7 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 0.9 % ±0.1 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 3380.5 MPa ±52.1 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 51.7 MPa ±0.6 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 5.5 kJ/m² ±0.2 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Fair | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |