| Manufacturer | Polymaker | |
| Product Name | PolyLite PLA Pro | |
| Filament Type | PLA | |
| Finish | Enhanced |
| Nozzle Temperature | 190-220 °C | |
| Bed Temperature | 30-60 °C | |
| Print Speed | 30-70 mm/s | |
| Cooling Fan | On | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-60 mm/s | |
| Build Surface Materials | Glass, PEI |
| Diameter | 1.75-2.85 mm ±0.03 | |
| Density | 1.22 g/cm³ | ISO1183, GB/T1033 |
| Melt Index | 6 g/10 min | 210°C, 2.16kg |
| Glass Transition Temperature | 62 °C | DSC, 10°C/min |
| Melting Temperature | 150 °C | DSC, 10°C/min |
| Vicat Softening Temperature | 62.7 °C | ISO 306, GB/T 1633 |
| Heat Deflection Temperature @ 1.8MPa | 57.6 °C | ISO 75 |
| Heat Deflection Temperature @ 0.45MPa | 59.3 °C | ISO 75 |
| Young's Modulus (X-Y) | 2932.2 MPa ±55.3 | ISO 527 |
| Young's Modulus (Z) | 2633 MPa ±117.4 | ISO 527 |
| Tensile Strength (X-Y) | 49.8 MPa ±0.4 | ISO 527 |
| Tensile Strength (Z) | 36.5 MPa ±0.6 | ISO 527 |
| Elongation at Break (X-Y) | 6.3 % ±0.9 | ISO 527 |
| Elongation at Break (Z) | 2.4 % ±0.3 | ISO 527 |
| Bending Modulus (X-Y) | 2933.8 MPa ±78.3 | ISO 178 |
| Bending Strength (X-Y) | 77.9 MPa ±0.4 | ISO 178 |
| Charpy Impact Strength (X-Y) | 17.1 kJ/m² ±1.2 | ISO 179 |
| Resistance to Acids | Not Resistant | Data Sheet |
| Resistance to Alkalis | Not Resistant | Data Sheet |
| Technical Data Sheet | View Data Sheet(Version v5.3) |