| Manufacturer | Polymaker | |
| Product Name | Polymaker Draft PLA | |
| Filament Type | PLA | |
| Finish | Standard |
| Nozzle Temperature | 190-230 °C | |
| Bed Temperature | 25-60 °C | |
| Print Speed | 50-300 mm/s | |
| Cooling Fan | ON | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s | |
| Support Material | PolySupport and PolyDissolve S1 |
| Density | 1.31 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 20 g/10 min | 210 °C, 2.16kg |
| Glass transition temperature | 62 °C | DSC, 10 °C/min |
| Melting temperature | 162 °C | DSC, 10 °C/min |
| Vicat softening temperature | 63 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 53 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 59 °C | ISO 75 |
| Young's modulus (X-Y) | 2190 MPa ±78 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1586 MPa ±84 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 24 MPa ±0.5 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 12 MPa ±0.5 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 23.9 % ±6 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 0.9 % ±0.1 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2707 MPa ±229 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 39.3 MPa ±0.6 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 6 kJ/m² ±0.5 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Fair | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |
| Safety Data Sheet | View Safety Sheet | Version 2.0 · 2024-11-19 |
| Polymaker Draft PLA TDS page on wiki.polymaker.com | Open link | |
| Polymaker Draft PLA on us.polymaker.com | Open link |