| Manufacturer | Polymaker | |
| Product Name | Polymaker Matte PLA for Production | |
| Filament Type | PLA | |
| Finish | Matte |
| Nozzle Temperature | 190-230 °C | |
| Bed Temperature | 25-60 °C | |
| Cooling Fan | ON | |
| Build Surface Materials | BuildTak, Glass, Blue Tape | |
| Support Material | PolySupport and PolyDissolve S1 |
| Density | 1.31 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 14-20 g/10 min | 210 °C, 2.16 kg |
| Glass transition temperature | 60.6 °C | DSC, 10 °C/min |
| Melting temperature | 162.6 °C | DSC, 10 °C/min |
| Vicat softening temperature | 62.7 °C | ISO 306, GB/T 1633 |
| Young's modulus (X-Y) | 1882 MPa ±141 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1869.7 MPa ±38 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 20.9 MPa ±2 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 18 MPa ±0.3 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 34.5 % ±8.1 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 2.51 % ±0.83 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2695 MPa ±541 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 39.6 MPa ±1.1 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 5.7 kJ/m² ±0.4 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Poor | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Poor | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.0 · 2026-09 |