| Manufacturer | Polymaker | |
| Product Name | PolyMax PLA | |
| Filament Type | PLA | |
| Finish | Nano-reinforced |
| Nozzle Temperature | 190-230 °C | |
| Bed Temperature | 25-60 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | ON | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s | |
| Support Material | PolySupport and PolyDissolve S1 |
| Density | 1.17-1.24 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 5-8 g/10 min | 210 °C, 2.16kg |
| Glass transition temperature | 61 °C | DSC, 10 °C/min |
| Melting temperature | 149 °C | DSC, 10 °C/min |
| Crystallization temperature | 112 °C | DSC, 10 °C/min |
| Vicat softening temperature | 62 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 52 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 55 °C | ISO 75 |
| Young's modulus (X-Y) | 2150.8 MPa ±67.8 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1983.6 MPa ±50.1 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 41.3 MPa ±2.2 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 32.4 MPa ±1.2 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 5.7 % ±0.8 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 4.7 % ±1.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2393.2 MPa ±195.2 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 62 MPa ±0.9 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 38.9 kJ/m² ±2.4 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Fair | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2019-07-29 |
| PolyMax PLA TDS page on wiki.polymaker.com | Open link | |
| PolyMax PLA on us.polymaker.com | Open link |