Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolySonic PLA Pro | |
| Filament Type | PLA | |
| Finish | Enhanced high-speed |
| Nozzle Temperature | 190-210 °C | |
| Bed Temperature | 30-60 °C | |
| Print Speed | 50-100 mm/s | |
| Cooling Fan | ON | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s | |
| Support Material | PolySupport and PolyDissolve S1 |
| Density | 1.23 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 15.5 g/10 min | 210 °C, 2.16 kg |
| Glass transition temperature | 61 °C | DSC, 10 °C/min |
| Melting temperature | 164 °C | DSC, 10 °C/min |
| Crystallization temperature | 96 °C | DSC, 10 °C/min |
| Decomposition temperature | 370 °C | TGA, 20 °C/min |
| Vicat softening temperature | 61 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 52 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 55 °C | ISO 75 |
| Young's modulus (X-Y) | 2360 MPa ±30.1 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2283.3 MPa ±32.1 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 41.2 MPa ±0.6 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 33.6 MPa ±0.5 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 23.4 % ±6.3 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 4.9 % ±1.1 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2688.7 MPa ±26.1 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 67.5 MPa ±0.7 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 22.7 kJ/m² ±2.5 | ISO 179, GB/T 1043 |
| Young's modulus (X-Y) (high speed) | 2305.7 MPa ±42.9 | ISO 527, GB/T 1040 |
| Young's modulus (Z) (high speed) | 2102.9 MPa ±74.3 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) (high speed) | 39.3 MPa ±0.5 | ISO 527, GB/T 1040 |
| Tensile strength (Z) (high speed) | 31.9 MPa ±0.5 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) (high speed) | 17.9 % ±5.2 | ISO 527, GB/T 1040 |
| Elongation at break (Z) (high speed) | 3.8 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) (high speed) | 2544.5 MPa ±27 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) (high speed) | 64.1 MPa ±0.6 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) (high speed) | 19.4 kJ/m² ±3.4 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Good | Data Sheet |
| Resistance to strong acids | Poor | Data Sheet |
| Resistance to weak alkalis | Fair | Data Sheet |
| Resistance to strong alkalis | Poor | Data Sheet |
| Resistance to oils and grease | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2023-03-23 |
| PolySonic PLA Pro TDS page on wiki.polymaker.com | Open link | |
| PolySonic PLA Pro on us.polymaker.com | Open link |