Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolyWood | |
| Filament Type | PLA | |
| Finish | Wood |
| Nozzle Temperature | 190-210 °C | |
| Bed Temperature | 25-60 °C | |
| Print Speed | 30-50 mm/s | |
| Cooling Fan | ON | |
| Retraction Distance | 3 mm | |
| Retraction Speed | 40 mm/s | |
| Build Surface Materials | BuildTak, Glass, Blue Tape | |
| Support Material | PolySupport and PolyDissolve S1 |
| Density | 0.8 g/cm³ | ISO 1183, GB/T 1033 |
| Glass transition temperature | 62.4 °C | DSC, 10 °C/min |
| Melting temperature | 150.8 °C | DSC, 10 °C/min |
| Crystallization temperature | 115.5 °C | DSC, 10 °C/min |
| Vicat softening temperature | 60.3 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 54.1 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 56.2 °C | ISO 75 |
| Young's modulus (X-Y) | 2636 MPa ±330 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 23.2 MPa ±0.4 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 14.5 MPa ±0.4 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 8.21 % ±0.87 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 7.91 % ±1.3 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2607 MPa ±50 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 52.9 MPa ±0.3 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 2.06 kJ/m² ±0.19 | ISO 179, GB/T 1043 |
| Resistance to weak acids | Not resistant | Data Sheet |
| Resistance to strong acids | Not resistant | Data Sheet |
| Resistance to weak alkalis | Not resistant | Data Sheet |
| Resistance to strong alkalis | Not resistant | Data Sheet |
| Resistance to organic solvents | No data available | Data Sheet |
| Resistance to oils and grease | No data available | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.1 · 2021-12 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2019-07-29 |
| PolyWood on us.polymaker.com | Open link |