Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | Fiberon PPS-CF10 | |
| Filament Type | PPS | |
| Finish | Carbon Fiber |
| Nozzle Temperature | 310-350 °C | |
| Bed Temperature | 80-90 °C | |
| Print Speed | 300 mm/s | |
| Cooling Fan | OFF |
| Density | 1.29 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 26.2 g/10 min | 300 °C, 2.16 kg |
| Glass transition temperature | 97.7 °C | DSC, 10 °C/min |
| Melting temperature | 279.7 °C | DSC, 10 °C/min |
| Crystallization temperature | 218.8 °C | DSC, 10 °C/min |
| Decomposition temperature | 502.7 °C | TGA, 20 °C/min |
| Vicat softening temperature | 267.5 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 133 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 252.5 °C | ISO 75 |
| Young's modulus (X-Y) | 5446.7 MPa ±149 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2790 MPa ±152.6 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 59.4 MPa ±1.3 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 32 MPa ±5.1 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 1.4 % ±0.1 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 1.6 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 4646.9 MPa ±136.9 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 2619.3 MPa ±155.3 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 94.3 MPa ±1.9 | ISO 306, GB/T 1633 |
| Bending strength (Z) | 30 MPa ±5.2 | ISO 306, GB/T 1633 |
| Notched Charpy impact strength (X-Y) | 5.3 kJ/m² ±0.2 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) | 11.4 kJ/m² ±0.7 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) | 4.1 kJ/m² ±1.3 | ISO 179, GB/T 1043 |
| Flame retardancy | V0 | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.1 · 2024-11 |
| Safety Data Sheet | View Safety Sheet | Version 2.0 · 2024-12 |
| Fiberon PPS-CF10 TDS page on wiki.polymaker.com | Open link | |