Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PolyCast | |
| Filament Type | PVB | |
| Finish | Castable |
| Nozzle Temperature | 190-220 °C | |
| Bed Temperature | 25-70 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | ON | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 20-40 mm/s | |
| Support Material | PolyDissolve S1 |
| Density | 1.1 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 6.6-6.7 g/10 min | 260 °C, 2.16kg |
| Glass transition temperature | 70 °C | DSC, 10 °C/min |
| Decomposition temperature | 260 °C | TGA, 20 °C/min |
| Vicat softening temperature | 67 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 53 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 67 °C | ISO 75 |
| Young's modulus (X-Y) | 2215 MPa ±42 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2111 MPa ±87 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 53.2 MPa ±1.1 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 26.3 MPa ±2.1 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 5.7 % ±0.5 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 1.3 % ±0.1 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 2233 MPa ±106 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 78 MPa ±2.3 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 2.9 kJ/m² ±0.3 | ISO 179, GB/T 1043 |
| Technical Data Sheet | View Data Sheet | Version 5.4 · 2024-11 |
| Safety Data Sheet | View Safety Sheet | Version 1.0 · 2019-07-29 |
| PolyCast TDS page on wiki.polymaker.com | Open link | |
| PolyCast on us.polymaker.com | Open link |