Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | ABS-GF25 Filament | |
| Filament Type | ABS | |
| Finish | Matte |
| Nozzle Temperature | 250-270 °C | |
| Bed Temperature | 100-110 °C | |
| Print Speed | 30-120 mm/s | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 1800-3600 mm/min | |
| Build Surface Materials | Glass, PEI Film, PC Film | |
| Support Material | QIDI S-White Quick-Remove Support Material |
| Density | 1.15 g/cm³ | ISO 1183 |
| Glass Transition Temperature | 103 °C | ISO 11357 |
| Melt Index | 4.2 g/10 min | |
| Heat Deflection Temperature @ 1.8MPa | 81 °C | ISO 75 Method A |
| Heat Deflection Temperature @ 0.45MPa | 87 °C | ISO 75 Method B |
| Tensile breaking strength (X-Y) | 48.48 MPa ±0.61 | ISO 527 |
| Elongation at Break (X-Y) | 2.1 % ±0.1 | ISO 527 |
| Young's Modulus (X-Y) | 3752.13 MPa ±68.39 | ISO 527 |
| Tensile breaking strength (Z) | 30.48 MPa ±0.47 | ISO 527 |
| Elastic Modulus (Z) | 2843.56 MPa ±69.9 | ISO 527 |
| Elongation at Break (Z) | 2.2 % ±0.44 | ISO 527 |
| Bending strength (X-Y) | 78.8 MPa ±1.26 | ISO 178 |
| Bending modulus (X-Y) | 3531.71 MPa ±75.79 | ISO 178 |
| Notched Charpy Impact Strength (X-Y) | 8.91 kJ/m² ±0.63 | ISO 179 |
| Glass Fiber Content | 25 % |
| Ventilation | Place the printer in a well-ventilated environment when printing ABS material. | Data Sheet |
| Surface Finish | Bright matte texture with no floating fibres on the surface. | Data Sheet |
| Low Warpage | Low shrinkage and warpage resistance; higher fibre content than ordinary ABS-GF improves warping resistance and rigidity. | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.0 · 2023-05 |