Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | Odorless-ABS Rapido Filament | |
| Filament Type | ABS | |
| Finish | Standard |
| Nozzle Temperature | 240-260 °C | |
| Bed Temperature | 100-110 °C | |
| Print Speed | 30-120 mm/s | |
| Retraction Distance | 1-5 mm | |
| Retraction Speed | 1800-3600 mm/min | |
| Build Surface Materials | Glass, PEI Film, PC Film | |
| Support Material | QIDI S-White Quick-Remove Support |
| Density | 1.05 g/cm³ | ISO 1183 |
| Glass Transition Temperature | 101 °C | ISO 11357 |
| Melt Index | 7.8 g/10 min | |
| Vicat Softening Temperature | 103 °C | ISO 306 |
| Heat Deflection Temperature @ 1.8MPa | 86 °C | ISO 75 Method A |
| Heat Deflection Temperature @ 0.45MPa | 92 °C | ISO 75 Method B |
| Tensile yield strength (X-Y) | 38.96 MPa ±0.33 | ISO 527 |
| Young's Modulus (X-Y) | 2384.22 MPa ±20 | ISO 527 |
| Tensile breaking strength (X-Y) | 33.36 MPa ±0.53 | ISO 527 |
| Elongation at Break (X-Y) | 5.77 % ±0.84 | ISO 527 |
| Tensile breaking strength (Z) | 32.25 MPa ±0.72 | ISO 527 |
| Elastic Modulus (Z) | 2201.74 MPa ±74.91 | ISO 527 |
| Elongation at Break (Z) | 2.7 % ±0.59 | ISO 527 |
| Bending strength (X-Y) | 67.81 MPa ±0.54 | ISO 178 |
| Bending modulus (X-Y) | 2400 MPa ±79.69 | ISO 178 |
| Notched Charpy Impact Strength (X-Y) | 20.03 kJ/m² ±1.32 | ISO 179 |
| Ventilation | Lower odour than similar ABS products, but still place the printer in a well-ventilated area during printing. | Data Sheet |
| Moisture Sensitivity | Low moisture sensitivity; no special moisture protection needed after opening, and no obvious stringing when printed after exposure to air. | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.2 · 2023-07 |