| Manufacturer | QIDI | |
| Product Name | ASA Filament | |
| Filament Type | ASA | |
| Finish | Standard |
| Nozzle Temperature | 240-260 °C | |
| Bed Temperature | 100-110 °C | |
| Print Speed | 30-120 mm/s | |
| Retraction Distance | 1-5 mm | |
| Retraction Speed | 1800-3600 mm/min | |
| Build Surface Materials | Glass, PEI Film, PC Film | |
| Support Material | QIDI S-White Quick-Remove Support |
| Density | 1.07 g/cm³ | ISO 1183 |
| Glass Transition Temperature | 98 °C | ISO 11357 |
| Melt Index | 5.6 g/10 min | |
| Vicat Softening Temperature | 101 °C | ISO 306 |
| Heat Deflection Temperature @ 1.8MPa | 83 °C | ISO 75 Method A |
| Heat Deflection Temperature @ 0.45MPa | 93 °C | ISO 75 Method B |
| Tensile yield strength (X-Y) | 38.5 MPa ±1.6 | ISO 527 |
| Young's Modulus (X-Y) | 2317 MPa ±246 | ISO 527 |
| Tensile breaking strength (X-Y) | 32.23 MPa ±1.13 | ISO 527 |
| Elongation at Break (X-Y) | 5.2 % ±1.4 | ISO 527 |
| Tensile breaking strength (Z) | 27.87 MPa ±0.42 | ISO 527 |
| Elastic Modulus (Z) | 2037 MPa ±64 | ISO 527 |
| Elongation at Break (Z) | 2.43 % ±0.27 | ISO 527 |
| Bending strength (X-Y) | 64.49 MPa ±1.3 | ISO 178 |
| Bending modulus (X-Y) | 2399 MPa ±147 | ISO 178 |
| Notched Charpy Impact Strength (X-Y) | 12.9 kJ/m² ±0.9 | ISO 179 |
| UV Resistance | Resists UV-induced degradation, aging and colour fading; excellent weather resistance, suitable for outdoor use. | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.1 · 2023-07 |