| Manufacturer | QIDI | |
| Product Name | QIDI ASA-CF20 Core | |
| Filament Type | ASA | |
| Finish | Matte |
| Nozzle Temperature | 250-280 °C | |
| Bed Temperature | 100-110 °C | |
| Print Speed | 30-250 mm/s | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 1800-3600 mm/min | |
| Build Surface Materials | PEI | |
| Support Material | QIDI S-Multi Quick-Remove Support Material |
| Density | 1.06 g/cm³ | ISO 1183 |
| Melt Index | 4.3 g/10 min | |
| Heat Deflection Temperature @ 1.8MPa | 95.8 °C | ISO 75 Method A |
| Heat Deflection Temperature @ 0.45MPa | 101.1 °C | ISO 75 Method B |
| Tensile strength (X-Y) | 50.06 MPa ±1 | ISO 527 |
| Young's Modulus (X-Y) | 4502.58 MPa ±103.44 | ISO 527 |
| Elongation at Break (X-Y) | 1.64 % ±0.11 | ISO 527 |
| Bending strength (X-Y) | 84.3 MPa ±1.37 | ISO 178 |
| Bending modulus (X-Y) | 4537.67 MPa ±264.85 | ISO 178 |
| Notched Charpy Impact Strength (X-Y) | 5.76 kJ/m² ±0.17 | ISO 179 |
| Tensile Strength (Z) | 31.03 MPa ±2.18 | ISO 527 |
| Elastic Modulus (Z) | 2570.8 MPa ±130.85 | ISO 527 |
| Elongation at Break (Z) | 1.5 % ±0.14 | ISO 527 |
| Carbon Fiber Content | 20 % |
| Ventilation | Place the printer in a well-ventilated environment when printing ASA material. | Data Sheet |
| UV Resistance | Resists UV-induced degradation, aging and colour fading; suitable for outdoor use. | Data Sheet |
| Surface Finish | Bright matte texture with no floating fibres on the surface. | Data Sheet |
| Low Warpage | Low shrinkage and warpage resistance; higher fibre content than ordinary ASA-GF/CF improves warping resistance and rigidity. | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.0 · 2023-12 |