Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | PAHT-GF | |
| Filament Type | PA | |
| Finish | Standard |
| Nozzle Temperature | 300-320 °C | |
| Bed Temperature | 70-90 °C | |
| Print Speed | 30-120 mm/s | |
| Cooling Fan | OFF | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 1800-3600 mm/min | |
| Support Material | QIDI S-PAHT Quick-Remove Support |
| Density | 1.27 g/cm³ | ISO 1183 |
| Water Absorption | 1.75 % | ISO 62: Method 1 |
| Melting Point | 237 °C | ISO 11357 |
| Melt Index | 7.6 g/10 min | |
| Glass Fiber Content | 15 % | |
| Heat Deflection Temperature @ 1.8MPa | 79.5 °C | ISO 75: Method A |
| Heat deflection temperature (1.8 MPa) (annealed) | 109.4 °C | ISO 75: Method A |
| Heat Deflection Temperature @ 0.45MPa | 83.4 °C | ISO 75: Method B |
| Heat deflection temperature (0.45 MPa) (annealed) | 180.2 °C | ISO 75: Method B |
| Tensile Strength | 86.49 MPa ±1.03 | ISO 527 |
| Tensile strength (X-Y) (annealed) | 90.5 MPa ±2.57 | ISO 527 |
| Tensile Strength (X-Y) - Moisture Conditioned | 81.91 MPa ±2.36 | ISO 527 |
| Young's Modulus (X-Y) | 5118.97 MPa ±296.57 | ISO 527 |
| Young's modulus (X-Y) (annealed) | 5375.42 MPa ±244.39 | ISO 527 |
| Young's Modulus (X-Y) - Moisture Conditioned | 5374.22 MPa ±168.08 | ISO 527 |
| Elongation at Break (X-Y) | 2.71 % ±0.28 | ISO 527 |
| Elongation at break (X-Y) (annealed) | 2.28 % ±0.1 | ISO 527 |
| Elongation at Break (X-Y) - Moisture Conditioned | 3.25 % ±0.14 | ISO 527 |
| Bending strength (X-Y) | 137.78 MPa ±2.35 | ISO 178 |
| Bending strength (annealed) | 140.77 MPa ±5.28 | ISO 178 |
| Flexural Strength - Moisture Conditioned | 126.96 MPa ±3.54 | ISO 178 |
| Bending modulus (X-Y) | 4135.14 MPa ±64.91 | ISO 178 |
| Bending modulus (annealed) | 4897.64 MPa ±136.4 | ISO 178 |
| Flexural Modulus - Moisture Conditioned | 3993.32 MPa ±165.99 | ISO 178 |
| Notched Charpy Impact Strength (X-Y) | 7.97 kJ/m² ±1.75 | ISO 179 |
| Notched Charpy impact strength (X-Y) (annealed) | 5.84 kJ/m² ±0.37 | ISO 179 |
| Notched Charpy impact strength (X-Y) (moisture conditioned) | 9.56 kJ/m² ±1.14 | ISO 179 |
| Tensile Strength (Z) | 59.58 MPa ±1.71 | ISO 527 |
| Elastic Modulus (Z) | 3952.22 MPa ±135.01 | ISO 527 |
| Elongation at Break (Z) | 1.78 % ±0.07 | ISO 527 |
| Moisture Sensitivity | Low: semi-aromatic polyamide base with saturated moisture absorption about one tenth of ordinary PA6 (per TDS); still keep dry. | Data Sheet |
| Wear Resistance | Low coefficient of friction, self-lubricating, excellent wear resistance (suits gears). | Data Sheet |
| Dimensional Stability | Good dimensional stability; no warpage or shrinkage during printing. | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.0 · 2023-07 |
| https://qidi3d.com/products/paht-gf-filament | Open link |