Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | PC/ABS-FR Filament | |
| Filament Type | PC-ABS | |
| Finish | Standard |
| Nozzle Temperature | 240-270 °C | |
| Bed Temperature | 100-110 °C | |
| Print Speed | 30-300 mm/s | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 1800-3600 mm/min | |
| Build Surface Materials | Glass, PEI Film, PC Film |
| Density | 1.19 g/cm³ | ISO 1183 |
| Glass Transition Temperature | 105 °C | ISO 11357 |
| Melt Index | 25 g/10 min | |
| Heat Deflection Temperature @ 1.8MPa | 83 °C | ISO 75 Method A |
| Heat Deflection Temperature @ 0.45MPa | 88 °C | ISO 75 Method B |
| Tensile yield strength (X-Y) | 52.51 MPa ±0.28 | ISO 527 |
| Young's Modulus (X-Y) | 2588.73 MPa ±64.81 | ISO 527 |
| Tensile breaking strength (X-Y) | 48.99 MPa ±1.2 | ISO 527 |
| Elongation at Break (X-Y) | 5.55 % ±0.99 | ISO 527 |
| Tensile breaking strength (Z) | 34.26 MPa ±0.84 | ISO 527 |
| Elastic Modulus (Z) | 2302.81 MPa ±46.92 | ISO 527 |
| Elongation at Break (Z) | 1.88 % ±0.11 | ISO 527 |
| Bending strength (X-Y) | 85.95 MPa ±0.83 | ISO 178 |
| Bending modulus (X-Y) | 2504.55 MPa ±22.88 | ISO 178 |
| Notched Charpy Impact Strength (X-Y) | 8.39 kJ/m² ±0.46 | ISO 179 |
| Flammability Rating | UL94 V-0 (2 mm thickness); UL94 5VB (2.5 mm thickness). Halogen-free flame retardant. | Data Sheet |
| Moisture Sensitivity | Sensitive to moisture; stringing and surface roughness if damp. | Data Sheet |
| Ventilation | Place the printer in a well-ventilated area when printing PC/ABS-FR. | Data Sheet |
| Technical Data Sheet | View Data Sheet | 2023-08 |