Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | PEBA 95A | |
| Filament Type | PEBA | |
| Finish | Standard |
| Nozzle Temperature | 230-260 °C | |
| Bed Temperature | 60-100 °C | |
| Print Speed | 30-120 mm/s | |
| Retraction Distance | 0.4-1 mm | |
| Retraction Speed | 1800-3600 mm/min | |
| Build Surface Materials | Glass, PEI Film, PC Film | |
| Support Material | QIDI PLA Basic; QIDI S-White support |
| Density | 1.01 g/cm³ | ISO 1183 |
| Shore Hardness | 95 Shore A | ISO 7619 |
| Melt Index | 30 g/10 min | |
| Water Absorption | 1.56 % | ISO 62: Method 1 |
| Vicat Softening Temperature | 102.8 °C | ISO 306 |
| Bayshore rebound | 70 % | ASTM D2632 |
| Tensile breaking strength (X-Y) | 32.58 MPa ±0.64 | ISO 527 |
| Elongation at Break (X-Y) | 1106.8 % ±65.66 | ISO 527 |
| Tensile stress at 100% (X-Y) | 9.17 MPa ±0.14 | ISO 527 |
| Tensile stress at 200% (X-Y) | 8.98 MPa ±0.05 | ISO 527 |
| Tensile stress at 300% (X-Y) | 9.69 MPa ±0.08 | ISO 527 |
| Moisture Sensitivity | Absorbs moisture readily when exposed to air; keep in a dry box and dry before printing if damp. | Data Sheet |
| Stretch Capability | Nylon-based elastomer with lower density, higher elasticity, better low-temperature performance and better chemical resistance than TPU (per TDS). | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.1 · 2026-01 |
| https://qidi3d.com/products/peba-95a | Open link |