| Manufacturer | QIDI | |
| Product Name | PET-GF Filament | |
| Filament Type | PET | |
| Finish | Matte |
| Nozzle Temperature | 280-320 °C | |
| Bed Temperature | 60-80 °C | |
| Print Speed | 30-120 mm/s | |
| Cooling Fan | OFF | |
| Retraction Distance | 1-3 mm | |
| Retraction Speed | 1800-3600 mm/min | |
| Build Surface Materials | PEI, PVP glue | |
| Support Material | QIDI S-Multi Quick-Remove Support |
| Glass Fiber Content | 15 % | |
| Density | 1.38 g/cm³ | ISO 1183 |
| Water Absorption | 0.5 % | ISO 62: Method 1 |
| Melting Point | 251 °C | ISO 11357 |
| Melt Index | 5.3 g/10 min | |
| Heat Deflection Temperature @ 1.8MPa | 99.1 °C | ISO 75: Method A |
| Heat Deflection Temperature @ 0.45MPa | 120.3 °C | ISO 75: Method B |
| Tensile Strength | 70.86 MPa ±2.86 | ISO 527 |
| Young's Modulus (X-Y) | 4130.13 MPa ±107 | ISO 527 |
| Elongation at Break (X-Y) | 2.56 % ±0.3 | ISO 527 |
| Bending strength (X-Y) | 114.87 MPa ±3 | ISO 178 |
| Bending modulus (X-Y) | 3650.32 MPa ±65.81 | ISO 178 |
| Notched Charpy Impact Strength (X-Y) | 6.56 kJ/m² ±0.68 | ISO 179 |
| Tensile Strength (Z) | 33.95 MPa ±2.38 | ISO 527 |
| Elastic Modulus (Z) | 3322.37 MPa ±94.04 | ISO 527 |
| Elongation at Break (Z) | 1.14 % ±0.11 | ISO 527 |
| Support Material | Compatible with QIDI S-Multi Quick-Remove Support Material | Data Sheet |