Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | PETG Basic | |
| Filament Type | PETG | |
| Finish | Standard |
| Nozzle Temperature | 240-260 °C | |
| Bed Temperature | 70-80 °C | |
| Print Speed | 30-50 mm/s | |
| Cooling Fan | 0-10% |
| Tensile Strength | 45.5 MPa ±6 | ISO 527 |
| Tensile Strength (Z) | 37.52 MPa ±6 | ISO 527 |
| Elongation at Break (X-Y) | 12.7 % ±2 | ISO 527 |
| Elongation at Break (Z) | 1.5 % ±1 | ISO 527 |
| Tensile modulus (X-Y) | 1756 MPa ±100 | ISO 527 |
| Tensile modulus (Z) | 1735.1 MPa ±100 | ISO 527 |
| Flexural strength (X-Y) | 68.3 MPa ±4 | ISO 178 |
| Flexural Strength (X-Z) | 63.3 MPa ±4 | ISO 178 |
| Flexural modulus (X-Y) | 1982.3 MPa ±100 | ISO 178 |
| Flexural Modulus (X-Z) | 1913.2 MPa ±100 | ISO 178 |
| Unnotched Charpy impact strength (X-Y) | 24.2 kJ/m² ±3.5 | ISO 179 |
| Unnotched Charpy impact strength (Z) | 10.8 kJ/m² ±2 | ISO 179 |
| Unnotched Izod impact (X-Y) | 29.6 kJ/m² ±3.5 | ISO 180 |
| Unnotched Izod impact (Z) | 7.8 kJ/m² ±2 | ISO 180 |
| Water Absorption | 0.06 % | ISO 62 |
| Density | 1.26 g/cm³ | ISO 1183 (immersion) |
| Melt Index | 10 g/10 min | ISO 1133 |
| Glass Transition Temperature | 81.6 °C | DSC, 10 °C/min |
| Decomposition Temperature | 387.5 °C | TGA, 20 °C/min |
| Vicat Softening Temperature | 78 °C | ISO 306 |
| Heat Deflection Temperature @ 1.8MPa | 69.8 °C | ISO 75 |
| Heat Distortion Temperature (Z) | 67.6 °C | ISO 75 |
| Heat Deflection Temperature @ 0.45MPa | 74.8 °C | ISO 75 |
| Effect of Weak Acids | Not Resistant | Data Sheet |
| Effect of Strong Acids | Not Resistant | Data Sheet |
| Effect of Weak Alkalis | Not Resistant | Data Sheet |
| Effect of Strong Alkalis | Not Resistant | Data Sheet |
| Chemical resistance: organic solvents | Not Resistant | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 2.1 · 2025-10 |
| https://qidi3d.com/products/petg-basic | Open link |