Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | PETG-CF | |
| Filament Type | PETG | |
| Finish | Matte |
| Nozzle Temperature | 240-270 °C | |
| Bed Temperature | 70-80 °C | |
| Print Speed | 40-150 mm/s | |
| Cooling Fan | 0-50% | |
| Build Surface Materials | PEI, Glue |
| Tensile Strength | 50-57 MPa | ISO 527 |
| Tensile Strength (Z) | 26-30 MPa | ISO 527 |
| Elongation at Break (X-Y) | 3-7 % | ISO 527 |
| Elongation at Break (Z) | 3-6 % | ISO 527 |
| Young's Modulus (X-Y) | 3400-3700 MPa | ISO 527 |
| Elastic Modulus (Z) | 1400-1600 MPa | ISO 527 |
| Impact strength (X-Y) | 20-30 kJ/m² | ISO 179 |
| Impact strength (Z-X) | 3-13 kJ/m² | ISO 179 |
| Notched Charpy Impact Strength (X-Y) | 3-7 kJ/m² | ISO 179 |
| Notched Charpy impact strength (Z) | 3-6 kJ/m² | ISO 179 |
| Flexural strength (X-Y) | 84-95 MPa | ISO 178 |
| Flexural strength (Z-X) | 43-54 MPa | ISO 178 |
| Flexural modulus (X-Y) | 3200-3400 MPa | ISO 178 |
| Flexural modulus (Z-X) | 1700-1800 MPa | ISO 178 |
| Diameter | 1.75 mm ±0.03 | EX1125 |
| Roundness | - | EX1125 |
| Glass Transition Temperature | 66 °C | ISO 11357 |
| Melt Index | 8-14 g/10 min | ISO 1133 |
| Heat Deflection Temperature | 77 °C | ISO 75 |
| Vicat Softening Temperature | 83 °C | ISO 306 |
| Density | 1.27-1.31 g/cm³ | ISO 1183 |
| Chemical resistance: water | Insoluble in water | Data Sheet |
| Surface Finish | Premium matte textured finish | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 2.1 · 2025-10 |
| https://qidi3d.com/products/petg-cf | Open link |