| Manufacturer | QIDI | |
| Product Name | PETG-GF | |
| Filament Type | PETG | |
| Finish | Standard |
| Nozzle Temperature | 250-275 °C | |
| Bed Temperature | 60-80 °C | |
| Print Speed | 150 mm/s | |
| Cooling Fan | 0-50% | |
| Build Surface Materials | PEI, Glue |
| Glass Fiber Content | 5 % | |
| Tensile Strength | 45-51 MPa | ISO 527 |
| Tensile Strength (Z) | 25-31 MPa | ISO 527 |
| Elongation at Break (X-Y) | 4-8 % | ISO 527 |
| Elongation at Break (Z) | 2-7 % | ISO 527 |
| Young's Modulus (X-Y) | 2200-2400 MPa | ISO 527 |
| Elastic Modulus (Z) | 1100-1400 MPa | ISO 527 |
| Impact strength (X-Y) | 23-35 kJ/m² | ISO 179 |
| Impact strength (Z-X) | 5-15 kJ/m² | ISO 179 |
| Notched Charpy Impact Strength (X-Y) | 4-6 kJ/m² | ISO 179 |
| Notched Charpy impact strength (Z) | 1-2 kJ/m² | ISO 179 |
| Flexural strength (X-Y) | 71-84 MPa | ISO 178 |
| Flexural strength (Z-X) | 27-52 MPa | ISO 178 |
| Flexural modulus (X-Y) | 2200-2700 MPa | ISO 178 |
| Flexural modulus (Z-X) | 1400-1700 MPa | ISO 178 |
| Diameter | 1.75 mm ±0.03 | EX1125 |
| Roundness | - | EX1125 |
| Glass Transition Temperature | 66 °C | ISO 11357 |
| Melt Index | 5-10 g/10 min | ISO 1133 |
| Heat Deflection Temperature | 76 °C | ISO 75 |
| Vicat Softening Temperature | 85 °C | ISO 306 |
| Density | 1.25-1.28 g/cm³ | ISO 1183 |
| Chemical resistance: water | Insoluble in water | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 2.1 · 2025-10 |