Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | PLA Matte Basic | |
| Filament Type | PLA | |
| Finish | Matte |
| Nozzle Temperature | 210-230 °C | |
| Bed Temperature | 50-60 °C | |
| Print Speed | 30-50 mm/s |
| Tensile Strength | 35.5 MPa ±6 | ISO 527 |
| Tensile Strength (Z) | 32.46 MPa ±6 | ISO 527 |
| Elongation at Break (X-Y) | 5.3 % ±3 | ISO 527 |
| Elongation at Break (Z) | 1.5 % ±1 | ISO 527 |
| Tensile Modulus (X-Y) | 2256.3 MPa ±100 | ISO 527 |
| Tensile Modulus (Z) | 2186.5 MPa ±100 | ISO 527 |
| Flexural Strength (X-Y) | 63.7 MPa ±4 | ISO 178 |
| Flexural Strength (Z) | 28.3 MPa ±4 | ISO 178 |
| Flexural Modulus (X-Y) | 2566.8 MPa ±100 | ISO 178 |
| Flexural Modulus (Z) | 2135.6 MPa ±100 | ISO 178 |
| Charpy Impact Strength (X-Y) | 19.4 kJ/m² ±2 | ISO 179 |
| Charpy Impact Strength (Z) | 2.6 kJ/m² ±1 | ISO 179 |
| Izod Impact Strength (X-Y) | 18.8 kJ/m² ±2 | ISO 180 |
| Izod Impact Strength (Z) | 4.3 kJ/m² ±1 | ISO 180 |
| Water Absorption | 0.42 % | ISO 62 |
| Density | 1.32 g/cm³ | ISO 1183 |
| Melt Index | 2-7 g/10 min | ISO 1133 |
| Glass Transition Temperature | 65.4 °C | DSC, 10 °C/min |
| Melting Point | 95.4 °C | DSC, 10 °C/min |
| Crystallization Temperature | 150 °C | DSC, 10 °C/min |
| Vicat Softening Temperature | 61.1 °C | ISO 306, GB/T 1633 |
| Heat Deflection Temperature @ 1.8MPa | 55 °C | ISO 75 |
| Heat Deflection Temperature @ 0.45MPa | 55.5 °C | ISO 75 |
| Effect of Weak Acids | Not Resistant | Data Sheet |
| Effect of Strong Acids | Not Resistant | Data Sheet |
| Effect of Weak Alkalis | Not Resistant | Data Sheet |
| Effect of Strong Alkalis | Not Resistant | Data Sheet |
| Chemical resistance: organic solvents | Not Resistant | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 2.1 · 2025-10 |
| PLA Matte Basic on qidi3d.com | Open link |