| Manufacturer | QIDI | |
| Product Name | PLA Rapido Filament | |
| Filament Type | PLA | |
| Finish | Standard |
| Nozzle Temperature | 200-240 °C | |
| Bed Temperature | 35-55 °C | |
| Print Speed | 300 mm/s | |
| Cooling Fan | ON | |
| Build Surface Materials | PEI frosted board |
| Melting Point | 160 °C | ISO 11357 |
| Glass Transition Temperature | 60 °C | ISO 11357 |
| Melt Index | 5-10 g/10 min | ISO 1133 |
| Heat Deflection Temperature @ 0.45MPa | 59 °C | ISO 75 |
| Vicat Softening Temperature | 73 °C | ISO 306 |
| Density | 1.21-1.23 g/cm³ | ISO 1183 |
| Tensile Strength | 42-48 MPa | ISO 527 |
| Elongation at Break (X-Y) | 10-15 % | ISO 527 |
| Emodulus (X-Y) | 2800-3100 MPa | ISO 527 |
| Impact strength (X-Y) | 19-23 kJ/m² | ISO 179 |
| Notch impact strength (X-Y) | 4-6 kJ/m² | ISO 179 |
| Maximum force, flexural test (X-Y) | 73-80 MPa | ISO 178 |
| Flexural Modulus | 3000-3200 MPa | ISO 178 |
| Tensile Strength (Z) | 26-29 MPa | ISO 527 |
| Elongation at Break (Z) | 3-5 % | ISO 527 |
| Emodulus (Z) | 2300-2600 MPa | ISO 527 |
| Impact strength (Z) | 4-14 kJ/m² | ISO 179 |
| Notch impact strength (Z) | 2-3 kJ/m² | ISO 179 |
| Maximum force, flexural test (Z) | 46-54 MPa | ISO 178 |
| Flexural Modulus (X-Z) | 2300-2700 MPa | ISO 178 |
| Diameter | 1.75 mm ±0.03 | EX1125 |
| Roundness | - | EX1125 |
| Solubility | Insoluble in water | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 05 · 2025-02 |