Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | TPU-Aero | |
| Filament Type | TPU | |
| Finish | Foamed |
| Nozzle Temperature | 230-270 °C | |
| Bed Temperature | 30-45 °C | |
| Print Speed | 100 mm/s | |
| Cooling Fan | On | |
| Retraction Distance | - | |
| Build Surface Materials | Glass, PC Film, Steel Plate with coating PVP glue, PEI film or PEI coated build surface (spray alcohol to help remove print parts) |
| Filament Density | 1.15 g/cm³ | ISO 1183 |
| Melt Index | 8 g/10 min | |
| Vicat Softening Temperature | 50.3-78.8 °C | ISO 306 |
| Shore Hardness | 66-82 A | ISO 7619 |
| Tensile Yield Strength | 3.22-5.98 MPa | ISO 527 |
| Tensile breaking strength (X-Y) | 3.59-9.8 MPa | ISO 527 |
| Elongation at Break (X-Y) | 452.13-598.69 % | ISO 527 |
| Diameter | 1.75 mm |
| Foaming Technology | Active foaming during printing; foaming ratio controlled by print temperature, giving different weight reduction and softness. | Data Sheet |
| Weight Reduction | Up to 50% lighter than ordinary TPU at maximum foaming rate. | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.2 · 2025-03 |
| TPU-Aero on qidi3d.com | Open link |