Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | QIDI | |
| Product Name | TPU95A-HF | |
| Filament Type | TPU | |
| Finish | Standard |
| Nozzle Temperature | 210-230 °C | |
| Bed Temperature | 20-50 °C | |
| Print Speed | 30-120 mm/s | |
| Cooling Fan | On | |
| Retraction Distance | 1-5 mm | |
| Retraction Speed | 1800-3600 mm/min | |
| Build Surface Materials | Glass, PEI Film, PC Film |
| Density | 1.15 g/cm³ | ISO 1183 |
| Shore Hardness | 95 A | ISO 7619 |
| Melt Index | 30 g/10 min | |
| Vicat Softening Temperature | 99 °C | ISO 306 |
| Tensile breaking strength (X-Y) | 31.81 MPa ±3.26 | ISO 527 |
| Elongation at Break (X-Y) | 471 % ±81 | ISO 527 |
| Tensile stress at 100% (X-Y) | 9.75 MPa ±0.16 | ISO 527 |
| Tensile stress at 200% (X-Y) | 12.2 MPa ±0.27 | ISO 527 |
| Tensile stress at 300% (X-Y) | 17 MPa ±0.49 | ISO 527 |
| High Flow Properties | Improved flowability: easier to extrude than conventional TPU of the same hardness; ≥100 mm/s on direct-drive extruders, 30-60 mm/s on Bowden extruders. | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 5.0 · 2023-07 |
| TPU95A-HF Filament on qidi3d.com | Open link |