Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Sunlu | |
| Product Name | PA6-CF | |
| Filament Type | PA | |
| Finish | Carbon Fiber |
| Nozzle Temperature | 270-290 °C | |
| Bed Temperature | 50-70 °C | |
| Print Speed | 50-100 mm/s | |
| Cooling Fan | On | |
| Retraction Distance | 0.8-1.2 mm | |
| Retraction Speed | 30-40 mm/s | |
| Build Surface Materials | Textured PEI |
| Tensile strength (X-Y) | 112 MPa ±10 | ISO 527-2 |
| Elongation at break (X-Y) | 12 % ±3 | ISO 527-2 |
| Flexural strength (X-Y) | 192 MPa ±20 | ISO 178 |
| Flexural modulus (X-Y) | 8600 MPa ±400 | ISO 178 |
| Notched Izod impact strength (X-Y) | 6.5 kJ/m² ±2 | ISO 180 |
| Unnotched Izod impact strength (Z-X) | 3.6 kJ/m² ±1.2 | ISO 180 |
| Shore hardness | 80 D | ISO 868 |
| Heat deflection temperature (0.45 MPa) | 203 °C ±3 | ISO 75 |
| Glass transition temperature | 65 °C | ISO 11357-2 |
| Melting temperature | 225 °C | ISO 11357-3 |
| Decomposition temperature (5 % weight loss) | 330 °C | ISO 11358 |
| Melt mass-flow rate | 16.5 g/10 min ±3 | ISO 1133 |
| Density | 1.12 g/cm³ | ISO 1183 |
| Flammability (UL 94) | HB | Data Sheet |
| Weak acids (pH 3-6) | Good | Data Sheet |
| Strong acids (pH <3) | Poor | Data Sheet |
| Weak bases (pH 8-10) | Excellent | Data Sheet |
| Strong bases (pH >10) | Good | Data Sheet |
| Deionized water | Excellent | Data Sheet |
| Alcohol (ethanol) | Fair | Data Sheet |
| Ketone (acetone) | Fair | Data Sheet |
| Petroleum fuels | Excellent | Data Sheet |
| Ester | Excellent | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version A/1 · 2026-03 |
| Safety Data Sheet | View Safety Sheet | Version 5.0 · 2024-05-30 |
| PA6-CF on sunlu.com | Open link |