Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Sunlu | |
| Product Name | PLA Carbon Fiber | |
| Filament Type | PLA | |
| Finish | Standard |
| Nozzle Temperature | 215-245 °C | |
| Bed Temperature | 50-60 °C | |
| Print Speed | 50-200 mm/s | |
| Cooling Fan | On | |
| Retraction Distance | 0.8-1.2 mm | |
| Retraction Speed | 30-40 mm/s | |
| Build Surface Materials | Textured PEI | |
| Support Material | PVA |
| Tensile strength (X-Y) | 44 MPa ±5 | ISO 527-2 |
| Elongation at break (X-Y) | 10.4 % ±3 | ISO 527-2 |
| Flexural strength (X-Y) | 79 MPa ±5 | ISO 178 |
| Flexural modulus (X-Y) | 3221 MPa ±200 | ISO 178 |
| Notched Izod impact strength (X-Y) | 3.5 kJ/m² ±1.5 | ISO 180 |
| Unnotched Izod impact strength (Z-X) | 5.5 kJ/m² ±2 | ISO 180 |
| Shore hardness | 84 D | ISO 868 |
| Heat deflection temperature (0.45 MPa) | 55.5 °C ±3 | ISO 75 |
| Glass transition temperature | 59 °C | ISO 11357-2 |
| Melting temperature | 168.6 °C | ISO 11357-3 |
| Decomposition temperature (5 % weight loss) | 367.7 °C | ISO 11358 |
| Vicat softening temperature | 54 °C | ISO 306 |
| Moulding shrinkage | 0.3-1.1 % | ISO 294 |
| Coefficient of thermal expansion | 101 µm/(m·°C) | ISO 11359-2 |
| Melt mass-flow rate | 20.4 g/10 min ±3 | ISO 1133 |
| Density | 1.23 g/cm³ | ISO 1183 |
| Flammability (UL 94) | HB | Data Sheet |
| Weak acids (pH 3-6) | Good | Data Sheet |
| Strong acids (pH <3) | Poor | Data Sheet |
| Weak bases (pH 8-10) | Good | Data Sheet |
| Strong bases (pH >10) | Poor | Data Sheet |
| Deionized water | Good | Data Sheet |
| Alcohol (ethanol) | Fair | Data Sheet |
| Ketone (acetone) | Poor | Data Sheet |
| Petroleum fuels | Good | Data Sheet |
| Ester | Good | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version A/1 · 2026-03 |
| Safety Data Sheet | View Safety Sheet | Version 5.3 · 2023-10-19 |
| PLA Carbon Fiber on sunlu.com | Open link |